Maxfire Blankets (1800ºF – 2600ºF Spun Insulation Blanket)

Maxfire Ceramic Blanket Products are comprised of high-strength ceramic fibers spun from alumina-silica, mechanically needled and cross-locked through a unique forming process, to produce a resilient blanket with unexcelled handling strength and surface integrity. All Ceramic Blanket Products are completely inorganic and available in a variety of densities, thickness and temperature capabilities. Maxfire Ceramic Blanket Products offer excellent thermal and acoustical performance, high temperature stability, low heat storage, thermal shock resistance and are unaffected by water or oil, with thermal and physical properties restored upon drying.

Specifications

Mean Fiber Diameter ( Microns )2.5 to 3.5
Melting Temperature ( ºC )1648
Melting Temperature ( ºF )2998
Shrinkage Rate ( % )≤ 3

Applications

  • Furnace, kiln, reformer and boiler linings
  • Investment casting mold and wrappings
  • Removable blankets for field stress relieving
  • Reusable insulation for steam and gas turbines
  • Flexible high temperature pipe insulation
  • Cryogenic insulation
  • Primary reformer header insulation
  • Incinerator equipment and stack linings
  • Annealing cover seals
  • Nuclear insulation applications
  • Fire protection
  • Ceramic fiber modules
  • High temperature kiln and furnace insulation
  • Furnace door linings and seals
  • Soaking pit seals
  • Furnace repairs
  • Thermal reactor insulation
  • Expansion joint packing and seals
  • High temperature gaskets
  • Glass furnace crown insulation
  • High temperature filtration
  • Atmosphere furnace lining
  • Field steam generator lining
  • Appliance insulation

Thermal Conductivity (k)

All heat flow calculations are based on a surfaccell namemissivity factor of 0.90, an ambient temperature of 80ºF, and zero wind velocity, unless otherwise stated. All thermal conductivity values have been measured in accordance with ASTM C 177. When comparing similar data, it is advisable to check the validity of all thermal conductivity values and ensure the resulting heat flow calculations are based on the same condition factors. Variations in any of these factors will result in significant differences in the calculatecell nameata.

Other Information

Combustibility – Rated noncombustible per ASTM E-136; BS476P4/DIN4102
Surface Burning Characteristics – Flame spread 0; Smoke developed 0, per ASTM E-84
Asbestos – Completely Asbestos Free

Safety First

Follow good safety and industrial hygiene practices during handling and installing of all products and systems. Take necessary precautions and wear the appropriate personal protectivcell namequipment as needed.
Read material safety data sheets and related literature on products before specification and/or installation.

General

The information presented herein represents typical or average values obtained by ASTM or other standard methods. The values will vary due to normal manufacturing variations. The person using this product must determine its suitability for a particular application.

Foundry Service, Inc. shall not be liable for incidental and consequential damages, directly or indirectly sustained, nor for any loss caused by application of these goods not in accordance with current printed instructions or for other than the intended use. Our liability is expressly limited to replacement of defective goods. Any claim shall be deemed waived unless made in writing to us within thirty (30) days from date it was or reasonably should have been discovered.