IFB-2600

Note: This is a variation of Insulating Fire Bricks.

Foundry Service supplies Insulating Fire Brick (IFB) for use in applications from 2300ºF (1100ºC) to 3200ºF (1760ºC). Each type is formulated to meet specific thermal and physical requirements, and after firing is machined to precise tolerances. Made from high purity refractory clays and other ceramic raw materials, these IFB contain carefully graded organic filler which is burned out during manufacture to give a uniform, controlled pore structure. Standard sizes are 9″ x 4.5″ x 2.5″ and 9″ x 4.5″ x 3″, but custom sizes up to 24″ x 9″ x 3″ can be produced without any cemented joints. Thicknesses up to 4 1/2″, along with widths up to 12″, allow a range of shapes and sizes for applications such as suspended roof modules. In addition to standard shapes including arches, wedges, soaps and splits, fabricated bricks are also available in special cemented or machined shapes. A large machine shop at the factory is capable of supplying accurate machined shapes of nearly any description. The unique large slab means that a finished shape will have fewer joints than shapes made from any other IFB manufacturer. IFB shapes with drilled holes, grooves, flycuts, tapers, radii cuts, skew planes, tongue and groove, notches and chord cuts arcell nameasily fabricated in any quality IFB.

Specifications

Standard Brick Sizes ( in )9 x 4.5 x 2.5
9 x 4.5 x 3
Composition1.1% TiO2
39% SiO2
57% Al2O3
Density ( lb/ft³ )50
Density ( kg/m³ )801
Maximum Operating Temperature ( ºC )1427
Maximum Operating Temperature ( ºF )2600
Modulus of Rupture ( MPa )1.38
Modulus of Rupture ( psi )200
Cold Crushing Strength ( MPa )1.79
Cold Crushing Strength ( psi )260