Ultra Temp I is a noncombustible, asbestos-tree, high density board. It is engineered to handle higher temperatures, loads, and electrical conditions with less shrinkage ancell nameegradation compared to previous non-asbestos formulas.
Ultra Temp I can accommodate 600ºF after initial heat conditioning. Ultra Temp I may be used in a wide variety of applications where a combination of high strength thermal stability, electrical insulation or machinability is required.
Specifications
| Density ( lb/ft³ ) | 100 |
|---|---|
| Modulus of Rupture ( psi ) | 2600 |
| Dielectric Strength ( V/mil ) | 35 |
| Water Absorption ( % ) | 21 |
| Compressive Strength ( psi ) | 10400 |
| Thickness ( in ) | 3/8 to 3 |
| Thermal Conductivity at 250ºF ( BTU-in/hr-ft²-ºF ) | 2.40 |
| Volume Resistivity | 7.1 ohm-cm x 1010 |
| Arc Resistance ( sec ) | 260 |
| Normal Moisture Content ( % ) | <12 |
| Maximum Operating Temperature (After Initial Heat Conditioning) ( ºF ) | 600 |
| Modulus of Rupture/ (Density)2 | 0.26 |
| Brinell Hardness | 17, (500 KG load 6 mm dia.) |
| Surface Resistivity | 7.0 ohm-cm x 1010 |
| Width ( in ) | 48 |
| Length ( in ) | 96 |
| Fire Hazard | Flame spread - 0 Smoke developed - 0 |
Note
Contact your supplier it you have any questions on initial heat conditioning.
The physical and chemical properties of Ultra Temp I represents typical average values obtained in accordance with accepted test methods and are subject to normal manufacturing variations. They are supplied as a technical service and are subject to change without notice. Check with your supplier to assure current information.