Fibercomp is an ultra high strength, high temperature carbon fiber reinforced thermoset Polyimide composites with unmatched strength-to-weight ratios. Some of the outstanding properties of these materials include: high temperature resistance, self lubricating, high impact strength, excellent corrosion resistance, low wear, light weight, and goocell nameimensional stability.
Specifications
| Density ( lb/ft³ ) | 95 |
|---|---|
| Maximum Operating Temperature ( ºF ) | 850 |
| Coefficient of Linear Thermal Expansion ( in/in/ºF ) | 10 x 10-6 |
| Specific Gravity | 1.50 |
| Chemical Resistance | Excellent (Strong Bases w/pH > 10 Not Recommended) |
| Machinability | Good |
| Maximum Sheet Size ( in ) | 20 x 30 |
| Thermal Conductivity ( BTU-in/hr-ft²-ºF ) | 8.3 |
| Continuous Operating Temperature ( ºF ) | 600 |
| Matrix | Polyimide Resin |
| Reinforcement | Carbon Fiber |
| Filler | Graphite Powder |
| Compressive Strength at 73ºF ( psi ) | 36000 |
| Compressive Strength at 500ºF ( psi ) | 25000 |
| Flexural Strength at 73ºF ( psi ) | 15000 |
| Flexural Strength at 500ºF ( psi ) | 12500 |
| Flexural Modulus at 73ºF ( psi ) | 2100000 |
| Flexural Modulus at 500ºF ( psi ) | 1500000 |
| Tensile Strength at 73ºF ( psi ) | 12000 |
| Tensile Strength at 500ºF ( psi ) | 8000 |
| Tensile Modulus at 73ºF ( psi ) | 2300000 |
| Tensile Modulus at 500ºF ( psi ) | 1600000 |
| IZOD Impact Strength (Notched) at 73ºF ( ft lb/in ) | 3 |
| Coefficient of Friction (Unlubricated Against Steel) | 0.10 to 0.20 |
| Limiting PV (Unlubricated Against Steel) | 80000 |
Note
The Fibercomp properties listed represent typical average values obtained in accordance with accepted test methods and are subject to normal manufacturing variations. They are supplied as a technical service and are subject to change without notice. Check with your supplier to assure current information
Available Forms
Custom Molded
Plates
Rods
Tubes