Mizzou Castable (3000ºF Industrial Grade High Strength Castable)

Note: This is a variation of Dense Castables.

Foundry Service sells only high quality, pure, high density castables (monolithic)suitable for high temperature structural applications. These dense castables are available in various grades suitable for a specific range of operational conditions. Our refractory castables are hydraulic setting and can be casted or molded to any shape. All of these castables can also be modified for gunning applications. Foundry Service can pre-cast and fire parts and shapes per customer suppliecell namerawings as well.

Specifications

CompositionAlumina
Calcium Oxide
Silica
Standard Packaging55# Bag
Maximum Operating Temperature ( ºF )3000
Density at 1500ºF ( lb/ft³ )139 to 143
Cold Crushing Strength (Dried 18-24 hrs. at 220ºF [104ºC]) ( MPa )34.2
Cold Crushing Strength (Dried 18-24 hrs. at 220ºF [104ºC]) ( psi )5000
Cold Crushing Strength (Fired 5 hrs. at 1500ºF [816ºC]) ( MPa )20.7
Cold Crushing Strength (Fired 5 hrs. at 1500ºF [816ºC]) ( psi )3000
Cold Crushing Strength (Fired 5 hrs. at Use Limit) ( MPa )24.9
Cold Crushing Strength (Fired 5 hrs. at Use Limit) ( psi )3600
Modulus of Rupture (Dried 18-24 hrs. at 220ºF [104ºC]) ( MPa )7.4
Modulus of Rupture (Dried 18-24 hrs. at 220ºF [104ºC]) ( psi )1075
Modulus of Rupture (Fired 5 hrs. at 1500ºF [816ºC]) ( MPa )4.9
Modulus of Rupture (Fired 5 hrs. at 1500ºF [816ºC]) ( psi )700
Modulus of Rupture (Fired 5 hrs. at Use Limit) ( MPa )6.6
Modulus of Rupture (Fired 5 hrs. at Use Limit) ( psi )950