Note: This is a variation of Dense Castables.
Foundry Service sells only high quality, pure, high density castables (monolithic)suitable for high temperature structural applications. These dense castables are available in various grades suitable for a specific range of operational conditions. Our refractory castables are hydraulic setting and can be casted or molded to any shape. All of these castables can also be modified for gunning applications. Foundry Service can pre-cast and fire parts and shapes per customer suppliecell namerawings as well.
Specifications
| Composition | Alumina Calcium Oxide Silica |
|---|---|
| Standard Packaging | 55# Bag |
| Maximum Operating Temperature ( ºF ) | 3000 |
| Density at 1500ºF ( lb/ft³ ) | 124 to 131 |
| Cold Crushing Strength (Dried 18-24 hrs. at 220ºF [104ºC]) ( MPa ) | 14.5 to 20.1 |
| Cold Crushing Strength (Dried 18-24 hrs. at 220ºF [104ºC]) ( psi ) | 2100 to 3000 |
| Cold Crushing Strength (Fired 5 hrs. at 1500ºF [816ºC]) ( MPa ) | 10.3 to 17.2 |
| Cold Crushing Strength (Fired 5 hrs. at 1500ºF [816ºC]) ( psi ) | 1500 to 2500 |
| Cold Crushing Strength (Fired 5 hrs. at Use Limit) ( MPa ) | 13.8 to 20.1 |
| Cold Crushing Strength (Fired 5 hrs. at Use Limit) ( psi ) | 2000 to 3000 |
| Modulus of Rupture (Dried 18-24 hrs. at 220ºF [104ºC]) ( MPa ) | 2.07 to 3.45 |
| Modulus of Rupture (Dried 18-24 hrs. at 220ºF [104ºC]) ( psi ) | 300 to 500 |
| Modulus of Rupture (Fired 5 hrs. at 1500ºF [816ºC]) ( MPa ) | 1.21 to 2.24 |
| Modulus of Rupture (Fired 5 hrs. at 1500ºF [816ºC]) ( psi ) | 175 to 325 |
| Modulus of Rupture (Fired 5 hrs. at Use Limit) ( MPa ) | 3.45 to 6.21 |
| Modulus of Rupture (Fired 5 hrs. at Use Limit) ( psi ) | 500 to 900 |